塑料增白粉OB厂家出售增白剂OB塑料荧光增白剂

-1

荧光增白剂OB-1是一种白色粉末，主要由苯乙烯和聚乙烯醇组成，主要用于增白纤维素类纤维和染料染色纤维材料，它具有良好的耐水性、耐洗涤性和耐磨性等特性，可显著提高纤维织物的亮度和色泽，使其具有良好的服装性能。它具有的抗褪色性，并且具有良好的耐气候性和耐氧化性，可显著提高纤维的耐久性和使用寿命。此外，它还可以改善纤维的柔软性，使其具有更好的穿着舒适性。



Fluorescent whitening agent OB-1 is a white powder mainly composed of styrene and polyvinyl alcohol. It is mainly used for whitening cellulose fibers and dyeing dyeing fibers. It has good water resistance, washing fastness and abrasion resistance, which can significantly improve the brightness and color of the fiber fabrics and make them have good clothing performance. It has excellent anti-fading performance and good weatherability and oxidation resistance, which can significantly improve the durability and service life of the fibers. In addition, it can also improve the softness of the fibers, making them more comfortable to wear.

应用方法：
推荐用量（每100KG物料加入增白剂OB的用量）
1.PVC：白色0.01—0.05%
透明0.001—0.001%（可提高PVC的光亮度）

荧光增白剂各型号粉体的作用原理：
荧光增白剂可以吸收不可见的紫外光（波长范围约为360-380），转换为波长较长的蓝光或紫色的可见光，因而可以补偿基质中不想要的微黄色，同时反射出比原来入射的波长范围的更多的可见光，从而使制品显得更白、更亮更鲜艳。其作用是把制品吸收的不可见的紫外线转变成紫蓝色的荧光，与原有的黄光互为补色成为白光，提高产品在日光下的白度。

对于合成材料的纺前增白，常用高纯度的荧光增白剂不添加助剂。荧光增白剂在下列情况下适宜于制成粉状剂型：
1、生产规模较小、间歇生产的企业，这种情况一般采用较经济的箱式干燥方式，干燥后多成块状，经干式粉碎后制成粉状。
2、荧光增白剂耐热温度低，不适宜于其他造粒方式。
3、有特定用途的荧光增白剂产品。
4、生产厂设备的局限，不具备其他造粒条件。

有些增白剂的应用需要增白剂耐高温，所以需要了解增白剂的熔点。平时我们看到的户外广告、店面招牌等，大部分都是塑料制品。对于这种长期置于户外的塑料，为了保持其色彩的艳丽，荧光增白剂各型号粉体具有很高的耐候性，也是长期使用不易变色发黄。
许多荧光增白剂在一定的加工温度时会部分溶解在塑料中，此时荧光增白剂容易在这些底物中发生迁移。因此，荧光增白剂要具备优良的耐迁移性，不能迁移或渗透到其他材料中。
与其他添加剂的化学惰性且相容性要好。塑料在加工时，必然会加入许多添加剂，从而影响塑料增白剂的增白剂效果。如果两者要同时使用，应当考虑它们的匹配性。

水性涂料由于具有较好的环保性，因此多用于室内装修，外观主要是以白色为主，不过白色的涂料厂家遇到的比较多的问题是白亮度不够，即使是添加了钛白粉依然达不到理想的效果。之所以添加了钛白粉白度还是上不去的原因是钛白粉的增白原理是物理遮盖，相当于基础白，属于填充类的，如果想在白的基础上更白更亮则需要添加水性荧光增白剂来解决。
水性荧光增白剂的外观为乳白色液体，在水性涂料中具有较好的分散效果，并且耐酸耐碱，对于水性涂料生产过程中的水质没有要求。只需少量，涂料的白亮度会提升，而且耐候好，可以防止涂料老化。