PTFE增强PA66 NILAMID A3 TF20 NC 1102泰科纳
| ISO | dry / cond | Unit | Test Standard |
| Density | 1250 / - | kg/m³ | ISO 1183 |
| Molding shrinkage, parallel | 1.9 - 2.3 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 1.9 - 2.3 | % | ISO 294-4, 2577 |
| Water absorption, 23°C-sat | 6.5 / * | % | ISO 62 |
| Humidity absorption, 23°C/50%RH | 1.6 / * | % | ISO 62 |
| Tensile modulus | 2800 / - | MPa | ISO 527-2/1A |
| Tensile stress at yield, 50mm/min | 68 / - | MPa | ISO 527-2/1A |
| Tensile strain at break, 50mm/min | 7 / - | % | ISO 527-2/1A |
| Charpy impact strength, 23°C | 60 / - | kJ/m² | ISO 179/1eU |
| Charpy impact strength, -30°C | 40 / - | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, 23°C | 3.5 / - | kJ/m² | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 3 / - | kJ/m² | ISO 179/1eA |
| Ball indentation hardness, 30s | 140 | MPa | ISO 2039-1 |
| DTUL at 1.8 MPa | 75 / * | °C | ISO 75-1, -2 |
| DTUL at 0.45 MPa | 160 / * | °C | ISO 75-1, -2 |
| Other | dry / cond | Unit | Test Standard |
| Continuous service temperature | 90 / * | °C | DIN/IEC 60216-1 |
PA66美国杜邦ST801特殊级 韧性 的耐冲击性。
PA66塑胶原料日本东丽CM3001G-30一般用途 玻纤增强30%。
PA66日本东丽CM3001-N CM3006标准级尼龙-66未强化。
PA66日本东丽CM3004G-30玻纤增强30%含卤阻燃级。
PA66日本东丽CM3004-V0尼龙66未强化，无卤阻燃级。
PA66塑胶原料日本旭化成1300G高强度 高刚性 玻纤增强33%。
PA66日本旭化成1300S平衡的流动性和机械性能。
PA66日本旭化成1402S具有良好的抗热老化性能。
PA66日本旭化成FR200 FR370阻燃级UL94 V-0；不含卤素和磷。
PTFE增强PA66 NILAMID A3 TF20 NC 1102泰科纳