原包德国朗盛热稳定PA6 Durethan BG30XH3.0LT激光焊接
PA 6, 30 % glass fibers/glass spheres, injection molding, heat-aging stabilized, low tendency to warp, NIR-laser transparent coloring (black)
| Property | Test Condition | Unit | Standard | |||
| d.a.m. | cond. | |||||
| Rheological properties | ||||||
| C | Molding shrinkage, parallel | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.5 | |
| C | Molding shrinkage, transverse | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.8 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.2 | ||
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.3 | ||
Mechanical properties (23 °C/50 % r. h.) | ||||||
| C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 6400 | 3100 |
| C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 120 | 65 |
| C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 4.0 | 10 |
| C | Tensile creep modulus | 1 h | MPa | ISO 899-1 | 2400 | |
| C | Tensile creep modulus | 1000 h | MPa | ISO 899-1 | 2000 | |
| C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 45 | 75 |
| C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 40 | 45 |
| C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | <10 | 10 |
| C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
| Charpy notched impact strength | -40 °C | kJ/m² | ISO 179-1eA | <10 | <10 | |
原包德国朗盛热稳定PA6 Durethan BG30XH3.0LT激光焊接