汉高汉高导电胶,赤峰厚膜汉高ABLESTIKJM7000导电胶

乐泰ABLESTIK JM 7000
氰酸酯
外观银
治疗热治疗
填料型银
●良好的附着力
●水分低
●离子杂质低
●可靠性高
●空洞少
●导电
●导热
应用模连接
基板氧化铝，镀金氧化铝

LOCTITE ABLESTIK JM 7000 die attach adhesive has been
formulated for use in high throughput die attach applications. This
material has been used successfully on rigid substrates with die sizes
up to 700 mils.
LOCTITE ABLESTIK JM 7000 has been approved by DESC and
Rome Laboratory for military products.

TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, HAAKE RV-20 Rotoviscometer, mPa·s (cP):
Cone 1º @ Shear rate 22 s
-1 9,000
Work Life @ 25°C, hours 8 to 16
Shelf Life @ -40°C (from date of manufacture), days 365
TYPICAL CURING PERFORMANCE
Cure Schedule
30 minutes @ 150°C
Suggested temperature cures are from 150 to 350ºC. For
applications requiring higher electrical conductivity, a cure cycle of 15
minutes @ 300ºC is recommended. Product properties will not be
reduced by subsequent post die attach thermal exposure, i.e.,
wirebond, and/or lid seal up to 370ºC.

TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150ºC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300ºC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300ºC
Chip Size: ROC
15 x 15 mm > 5
BLETHERM 2600AT高导热导电银胶 黏 度： 8.5 PaS 剪切强度： - Mpa 工作时间： 1440 min 工作温度： - ℃ 保 质 期： 12 个月 固化条件： 30分钟升到200°C + 15分钟 @ 200°C 主要应用： 大功率LED

HENKEL ABLETHERM 2600AT粘合剂是一款特别为芯片需要高散而开发的芯片粘接胶,如大功率和和散热元气件. 本粘合剂是一种特的悬浮液-银和树脂颗粒悬浮在溶剂载体中. 一旦胶水完全固化,溶剂也会干掉, 本粘合剂含有很高比重的银. 本品主要用于高功率,高导热的大功率发光二极管.
Ablestik 84-1LMISR4是一种单组份、低粘度的导电银胶。胶流变性能好，适用于高速die attach封装，无拉丝和拖尾；纯度高，广泛应用在半导体工业主要用于半导体芯片的粘贴，适用于全自动机器高速点胶，是目前世界上出胶速度 快的一款导电银胶。特点 流变性能好，适用于高速die attach封装，无拉丝和拖尾；纯度高，广泛应用在半导体工业.

84-1 LMISR4导电银胶适用于全自动机器高速点胶。Ablebond 84-1 LMISR4导电银胶允许 少量胶分配，并降低停留时间，而无残胶或拉丝的烦恼。

包装规格：5cc 10cc



ABLESTIK 84-1A，84-1LMIT1,84-3等

ABLESTIK 5020 506胶膜

深圳汉高导电胶 西安汉高导电胶 沈阳汉高代理 山东汉高代理 西安导电胶 山东导电胶 广州导电胶 导电胶