沙伯基础无溴阻燃PBT/PC XENOY IQNH2900
Density / Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 26 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 2 | 2480 | MPa | ASTM D638 |
Tensile Strength 3 | ASTM D638 | ||
Yield | 63.0 | MPa | |
Break | 42.0 | MPa | |
Tensile Elongation 3 | ASTM D638 | ||
Yield | 4.0 | % | |
Break | 65 | % | |
Flexural Modulus 4 (50.0 mm Span) | 2240 | MPa | ASTM D790 |
Flexural Strength 4 (Yield, 50.0 mm Span) | 89.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact (23°C) | 550 | J/m | ASTM D256 |
Instrumented Dart Impact (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 77.0 | °C | ASTM D648 |
Vicat Softening Temperature | 100 | °C | ASTM D1525 5 |
RTI Elec 6 | 75.0 | °C | UL 746 |
RTI Imp 6 | 75.0 | °C | UL 746 |
RTI Str 6 | 75.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
Flame Rating | UL 94 | ||
> 1.1 mm | V-1 | ||
> 1.5 mm | V-0 | ||
> 2.5 mm | 5VB |
沙伯基础无溴阻燃PBT/PC XENOY IQNH2900