≥ 10千克¥25.00
低合金耐热钢TIG焊丝
类别 | 品名 | AWS型号 | 焊棒和焊丝化学成分(%) | 熔敷金属力学性能 | 特征与用途 | ||||||||||||||
C | Si | Mn | P | S | Cr | Mo | Ni | Nb | V | Cu | Al | σ0.2(MPa) | δb(MPa) | δ(%) | Akv(J) | ||||
TIG焊丝 | TGS-1CM | ER80S-G | 0.08 | 0.52 | 1.10 | 0.007 | 0.009 | 1.40 | 0.55 | 0.02 | 0.11 | 540 | 630 | 28 | 0℃:270 | 用于焊接ASTMA387Gr.11,Gr.12钢和类似钢种 | |||
TGS-1CML | ER90S-G | 0.03 | 0.50 | 1.13 | 0.005 | 0.009 | 1.40 | 0.49 | 0.04 | 0.12 | 480 | 580 | 31 | 0℃:300 | 适于焊接ASTMA387Gr.11,Gr.12钢和类似钢种,与TGS-1CM相比,TGS-1CML的含碳量较低 | ||||
TGS-2CM | ER90S-G | 0.11 | 0.36 | 0.75 | 0.004 | 0.008 | 2.29 | 1.07 | 0.05 | 0.12 | 610 | 720 | 28 | 0℃:250 | 适于焊接ASTMA387Gr.22钢和类似是而非钢种 | ||||
TGS-2CML | ER90S-G | 0.03 | 0.50 | 1.14 | 0.007 | 0.009 | 2.33 | 1.09 | 0.03 | 0.12 | 520 | 630 | 28 | 0℃:250 | 适于焊接ASTMA387Gr.22钢和类似的钢种,与TGS-2CM相比,TGS-2CML的含碳量较低 | ||||
TGS-9CM | ER80S-B8 | 0.07 | 0.39 | 0.52 | 0.006 | 0.009 | 8.98 | 1.00 | 0.18 | 0.12 | 410 | 590 | 32 | 0℃:220 | 适于焊接ASTMA387Gr.9钢和类似的钢种 | ||||
TGS-9Cb | ER90S-G | 0.08 | 0.16 | 1.01 | 0.006 | 0.005 | 9.01 | 0.90 | 0.71 | 0.04 | 0.18 | 0.15 | 700 | 780 | 24 | 0℃:240 | 适于焊接ASTMA387Gr.91钢和类似的钢种,焊缝金属具有优良的抗蠕变断裂性能 | ||
TGS-90B9 | ER90S-B9 | 0.12 | 0.17 | 1.04 | 0.007 | 0.005 | 9.14 | 0.91 | 0.93 | 0.16 | 0.10 | 756 | 851 | 23 | 0℃:172 | 可用于焊接ASTMA387Gr.91钢和类似钢种,焊缝金属具有优良的抗蠕变断裂性能,它符合AWSA5.28 ER90S-B9 | |||
TGS-56 | ER80S-G | 0.10 | 0.41 | 1.59 | 0.007 | 0.007 | 0.50 | 0.66 | 520 | 590 | 31 | -12℃:290 | 用于焊接Mn-Mo钢和Mn-Mo-Ni钢 | ||||||
TGS-3CMH | 0.12 | 0.18 | 0.45 | 0.005 | 0.008 | 3.02 | 1.02 | 0.01 | 600 | 720 | 25 | -18℃:320 | 用于焊接0.5%Mo钢 | ||||||
TGS-5CM | ER80S-B6 | 0.09 | 0.41 | 0.49 | 0.006 | 0.009 | 5.44 | 0.55 | 0.04 | 480 | 600 | 26 | 0℃:280 | 用于焊接5%Cr-0.5%Mo钢 | |||||
TGS-2CW | 0.04 | 0.41 | 0.45 | 0.005 | 0.004 | 2.32 | 0.52 | 467 | 578 | 31 | 0℃:205 | 用于焊接T23管子和P23管道 |