原包Ascend美国玻纤增强阻燃PA66 Vydyne 909
Vydyne 909 is an halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016") thick.
Density | 1.47 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow : 23°C, 2.00 mm | 1.0 | -- | % | |
Flow : 23°C, 2.00 mm | 0.40 | -- | % |
Tensile Modulus (23°C) | 9100 | 7100 | MPa | ISO 527-2 |
Tensile Stress (Break, 23°C) | 132 | 90.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 2.2 | 3.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 8300 | 5000 | MPa | ISO 178 |
Flexural Strength (23°C) | 193 | 140 | MPa | ISO 178 |
Poisson&＃39;s Ratio | 0.40 | -- | ISO 527-2 | |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 9.5 | -- | kJ/m² | |
23°C | 9.4 | -- | kJ/m² |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 230 | -- | °C | ISO 75-2/A |
Melting Temperature | 250 | -- | °C | ISO 11357-3 |
PA66（聚酰胺66或尼龙66），同PA6相比，PA66更广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。