汉高汉高导电胶,松江半导体材料汉高ABLESTIKJM7000导电胶

乐泰ABLESTIK JM 7000
氰酸酯
外观银
治疗热治疗
填料型银
●良好的附着力
●水分低
●离子杂质低
●可靠性高
●空洞少
●导电
●导热
应用模连接
基板氧化铝，镀金氧化铝

TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, HAAKE RV-20 Rotoviscometer, mPa·s (cP):
Cone 1º @ Shear rate 22 s
-1 9,000
Work Life @ 25°C, hours 8 to 16
Shelf Life @ -40°C (from date of manufacture), days 365
TYPICAL CURING PERFORMANCE
Cure Schedule
30 minutes @ 150°C
Suggested temperature cures are from 150 to 350ºC. For
applications requiring higher electrical conductivity, a cure cycle of 15
minutes @ 300ºC is recommended. Product properties will not be
reduced by subsequent post die attach thermal exposure, i.e.,
wirebond, and/or lid seal up to 370ºC.

TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of Thermal Expansion, :
Below Tg, ppm/°C 33
Glass Transition Temperature (Tg) by TMA, °C 240
Bulk Thermal Conductivity, W/(m-K):
@ 90°C 1.1
@ 165°C 1.0
Tensile Modulus, DMTA :
Cured 30 minutes @ 300ºC N/mm² 10,000
(psi) (1,450,377)
Extractable Ionic Content, @ 100°C:
Chloride (Cl-) <10
Sodium (Na+) <15
Potassium (K+) <15
Decomposition (in N2):
TGA analysis @ 10ºC/ minute ramp from 25 to 400
ºC
@ 340ºC, % 0.2
@ 400ºC, % 0.3
Electrical Properties
Sample cured 30 minutes @ 300ºC
Volume Resistivity, ohm-cm ≤0.01

TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150ºC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300ºC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300ºC
Chip Size: ROC
15 x 15 mm > 5
BLETHERM 2600AT高导热导电银胶 黏 度： 8.5 PaS 剪切强度： - Mpa 工作时间： 1440 min 工作温度： - ℃ 保 质 期： 12 个月 固化条件： 30分钟升到200°C + 15分钟 @ 200°C 主要应用： 大功率LED

HENKEL ABLETHERM 2600AT粘合剂是一款特别为芯片需要高散而开发的芯片粘接胶,如大功率和和散热元气件. 本粘合剂是一种特的悬浮液-银和树脂颗粒悬浮在溶剂载体中. 一旦胶水完全固化,溶剂也会干掉, 本粘合剂含有很高比重的银. 本品主要用于高功率,高导热的大功率发光二极管.
安徽ablestik 5020胶膜 506胶膜 安徽汉高代理 上海汉高代理 苏州汉高代理 安徽导电胶 安徽乐泰代理 北京乐泰导电胶