德国朗盛 PA6
B26S，B40SK、BG-50S、 BKV30SQ、BC30、BC304、BKV130H1.0、BKV130H2.0、
BKV15、BKV15H1.0、BKV15H2.0、BKV30H2.0、BKV30H2.0EF
PA性质：结晶性热可塑性塑料，有明显熔点，Nylon6 Tm为220-230℃，Nylon66则为260-270，Nylon本身具吸水基故有吸水性，成形前须干燥，温度过高干燥则尼龙粒变色。
优点：1、具高抗张强度；2、耐韧、耐冲击性特优；3、自润性、耐磨性佳、耐药品性优；4、低温特性佳；5、具自熄性
用途：电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输
分类：防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。

Durethan AKV 15 H3.0 000000 PA 66, 15% glass fibers, injection molding, heat-aging stabilized.
Durethan AKV 25 F30 000000 PA 66, 25 % glass fibers, injection molding, flame retardant
Durethan AKV 30 000000 PA 66, 30 % glass fibers, injection molding
Durethan AKV 30 G H2.0 SR1 900051
PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish.
Durethan AKV 30 G HR DUS023 900116
PA 66, 30 % glass fibers, injection molding, improved flowability, hydrolysis stabilized, improved surface finish, GIT/WIT
Durethan AKV 30 GIT H2.0 900116 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, GIT/WIT
Durethan AKV 30 H2.0 901510 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized
Durethan AKV 30 H3.0 000000
PA 66, 30 % glass fibers, injection molding, heat-aging stabilized
Durethan AKV 30 HR H2.0 901510 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized
Durethan AKV 325 H2.0 901510 PA 66, 25 % glass fibers, extrusion, blow molding, heat-aging stabilized, hydrolysis stabilized Applications: Profiles, hollow parts and pipes for the automotive cooling circuit
Durethan AKV 35 000000 PA 66, 35% glass fibers, injection molding
Durethan AKV 35 CX H2.0 900876 PA 66, 35 % glass fibers, injection molding, heat aging stabilized Applications: Chemically or physically (MuCell process) foamed applications like engine and valve covers
Durethan AKV 35 H2.0 901510 PA 66, 35 % glass fibers, injection molding, heat-aging stabilized Applications: gearbox oil sumps, oil modul
Durethan AKV35 H2.0 SR1 901510 PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, improved surface finish
Durethan AKV 35 H3.0 000000
PA 66, 35 % glass fibers, injection molding, heat-aging stabilized
Durethan AKV 35 HR H2.0 901510
PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized
Durethan AKV 35 LT H3.0 000000
PA 66, 35% glass fibers, injection molding, laser-transparent, heat-aging resistance
Durethan AKV 40 H2.0 901510
PA 66, 40 % glass fibers, injection molding, heat-aging stabilized
Durethan AKV 40 H3.0 000000 PA 66, 40 % glass fibers, injection molding, heat-aging stabilized
Durethan AKV 50 000000 PA 66, 50% glass fibers, injection molding
Durethan AKV 50 H2.0 901510 PA 66, 50 % glass fibers, injection molding, heat-aging stabilized
Durethan AKV 50 H3.0 000000 PA 66, 50 % glass fibers, injection molding, heat-aging stabilized
Durethan AM 40 X H2.0 901510 PA 66, 40 % glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warp
Durethan B 30 S 000000 PA 6, non-reinforced, injection molding
Durethan B 30 S F30 000000 PA 6, non-reinforced, injection molding, flame retardant
Durethan B 30 S FN30 000000 PA 6, non-reinforced, injection molding, halogen free flame retardant, heat-aging resistance


原料物性描述
PA6 聚酰胺6或尼龙6化学和物理特性 PA6的化学物理特性和PA66很相似，然而，它的熔点较低，而且工艺温度范围很宽。它的抗冲击性和抗溶解性比PA66要好,但吸湿性也更强。因为塑件的许多品质特性都要受到吸湿性的影响，因此使用PA6设计产品时要充分考虑到这一点。为了提高PA6的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。 对于没有添加剂的产品，PA6的收缩率在1%到1.5%之间。加入玻璃纤维添加剂可以使收缩率降低到0.3%（但和流程相垂直的方向还要稍高一些）。成型组装的收缩率主要受材料结晶度和吸湿性影响。实际的收缩率还和塑件设计、壁厚及其它工艺参数成函数关系。 对于没有添加剂的产品，PA6的收缩率在1%到1.5%之间。加入玻璃纤维添加剂可以使收缩率降低到0.3%（但和流程相垂直的方向还要稍高一些）。成型组装的收缩率主要受材料结晶度和吸湿性影响。实际的收缩率还和塑件设计、壁厚及其它工艺参数成函数关系。

注塑模工艺条件

干燥处理：由于PA6很容易吸收水分，因此加工前的干燥特别要注意。如果材料是用防水材料包装供应的，则容器应保持密闭。如果湿度大于0.2%，建议在80C以上的热空气中干燥16小时。如果材料已经在空气中暴露超过8小时，建议进行105C，8小时以上的真空烘干。

熔化温度：230~280C，对于增强品种为250~280C。 模具温度：80~90C。模具温度很显著地影响结晶度，而结晶度又影响着塑件的机械特性。对于结构部件来说结晶度很重要，因此建议模具温度为80~90C。对于薄壁的，流程较长的塑件也建议施用较高的模具温度。增大模具温度可以提高塑件的强度和刚度，但却降低了韧性。如果壁厚大于3mm，建议使用20~40C的低温模具。对于玻璃增强材料模具温度应大于80C。

注射压力：一般在750~1250bar之间（取决于材料和产品设计）。

注射速度：高速（对增强型材料要稍微降低）。 流道和浇口:由于PA6的凝固时间很短，因此浇口的位置非常重要。浇口孔径不要小于0.5*t（这里t为塑件厚度）。如果使用热流道，浇口尺寸应比使用常规流道小一些，因为热流道能够帮助阻止材料过早凝固。如果用潜入式浇口，浇口的小直径应当是0.75mm。典型用途 由于有很好的机械强度和刚度被广泛用于结构部件。由于有很好的耐磨损特性，还用于制造轴承