供应沙伯基础SE1GFN2玻纤增强阻燃PPO聚苯醚

Nominal Value

Unit

Test Method

Density / Specific Gravity

1.23

g/cm³

Molding Shrinkage - Flow (3.20 mm)

0.20 to 0.50

%

Water Absorption (24 hr)

0.060

%

Nominal Value

Unit

Test Method

Tensile Strength ² (Break)

107

MPa

Tensile Elongation ² (Break)

5.0

%

Flexural Modulus ³ (100 mm Span)

5720

MPa

Flexural Strength ³ (Yield, 100 mm Span)

152

MPa

Nominal Value

Unit

Test Method

Notched Izod Impact

-40°C

96

J/m

23°C

110

J/m

Nominal Value

Unit

Test Method

Rockwell Hardness (L-Scale)

106

Nominal Value

Unit

Test Method

Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm)

138

°C

Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm)

132

°C

CLTE - Flow (-40 to 95°C)

3.6E-5

cm/cm/°C

RTI Elec

110

°C

RTI Imp

105

°C

RTI Str

110

°C

Nominal Value

Unit

Test Method

Dielectric Strength (3.20 mm, in Oil)

24

kV/mm

Dielectric Constant

50 Hz

2.98

60 Hz

2.98

Dissipation Factor

50 Hz

1.6E-3

60 Hz

1.6E-3

Arc Resistance ⁴

PLC 7

Comparative Tracking Index (CTI)

PLC 1

High Amp Arc Ignition (HAI)

PLC 1

High Voltage Arc Tracking Rate (HVTR)

PLC 4

Hot-wire Ignition (HWI)

PLC 0

Nominal Value

Unit

Test Method

Flame Rating

1.5 mm

V-1

6.0 mm

V-0

2.5 mm

5VA

Oxygen Index

31

%