PA66美国杜邦10B140BK061杜邦尼龙66,PA66塑胶原料,PA66聚酰胺

DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data**)

Nylon 66, 40% Mineral Filled

--



产品说明

Minlon® 10B140 BK061 is a 40% mineral reinforced, black polyamide 66 resin for injection molding. It has very low warpage.
Information provided by DuPont Performance Polymers


DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data**) 物性表


物理性能

额定值 (公制)

额定值 (英制)

测试方法

密度 1.50 g/cc 0.0542 lb/in³ DAM; ISO 1183
填料含量 40 % 40 % DAM
Water Absorption 1.6 %
@Temperature 23.0 °C
1.6 %
@Temperature 73.4 °F
Equilibrium 50%RH; DAM; ISO 62, Similar to
5.0 %
@Temperature 23.0 °C
5.0 %
@Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to


机械性能

额定值 (公制)

额定值 (英制)

测试方法

抗张强度(断裂) 54.0 MPa
@Temperature 23.0 °C
7830 psi
@Temperature 73.4 °F
50%RH; ISO 527
82.0 MPa
@Temperature 23.0 °C
11900 psi
@Temperature 73.4 °F
DAM; ISO 527
伸长率 (断裂) 3.5 %
@Temperature 23.0 °C
3.5 %
@Temperature 73.4 °F
DAM; ISO 527
9.0 %
@Temperature 23.0 °C
9.0 %
@Temperature 73.4 °F
50%RH; ISO 527
拉伸模量 3.80 GPa
@Temperature 23.0 °C
551 ksi
@Temperature 73.4 °F
50%RH; ISO 527
6.60 GPa
@Temperature 23.0 °C
957 ksi
@Temperature 73.4 °F
DAM; ISO 527
悬壁梁缺口冲击强度 3.50 kJ/m²
@Temperature 23.0 °C
1.67 ft-lb/in²
@Temperature 73.4 °F
DAM; ISO 180/1A
4.00 kJ/m²
@Temperature 23.0 °C
1.90 ft-lb/in²
@Temperature 73.4 °F
50%RH; ISO 180/1A
简支梁无缺口冲击强度 3.50 J/cm²
@Temperature 23.0 °C
16.7 ft-lb/in²
@Temperature 73.4 °F
DAM; ISO 179/1eU
6.00 J/cm²
@Temperature 23.0 °C
28.6 ft-lb/in²
@Temperature 73.4 °F
50%RH; ISO 179/1eU
简支梁缺口冲击强度 0.350 J/cm²
@Temperature 23.0 °C
1.67 ft-lb/in²
@Temperature 73.4 °F
DAM; ISO 179/1eA
0.450 J/cm²
@Temperature 23.0 °C
2.14 ft-lb/in²
@Temperature 73.4 °F
50%RH; ISO 179/1eA


热性能

额定值 (公制)

额定值 (英制)

测试方法

熔融温度 263 °C 505 °F 10°C/min; DAM; ISO 11357-1/-3
载荷下热变形温度(0.46 MPa) 240 °C 464 °F DAM; ISO 75-1/-2
载荷下热变形温度(1.8 MPa) 170 °C 338 °F DAM; ISO 75-1/-2
UL RTI 105 °C
@Thickness 0.710 mm
221 °F
@Thickness 0.0280 in
DAM; UL 746B
120 °C
@Thickness 3.00 mm
248 °F
@Thickness 0.118 in
DAM; UL 746B
120 °C
@Thickness 1.50 mm
248 °F
@Thickness 0.0591 in
DAM; UL 746B
UL RTI，机械冲击 65.0 °C
@Thickness 0.710 mm
149 °F
@Thickness 0.0280 in
DAM; UL 746B
105 °C
@Thickness 1.50 mm
221 °F
@Thickness 0.0591 in
DAM; UL 746B
115 °C
@Thickness 3.00 mm
239 °F
@Thickness 0.118 in
DAM; UL 746B
UL RTI，机械无冲击 65.0 °C
@Thickness 0.710 mm
149 °F
@Thickness 0.0280 in
DAM; UL 746B
115 °C
@Thickness 1.50 mm
239 °F
@Thickness 0.0591 in
DAM; UL 746B
115 °C
@Thickness 3.00 mm
239 °F
@Thickness 0.118 in
DAM; UL 746B
可燃性(UL94) HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
DAM; UL94
HB
@Thickness 0.710 mm
HB
@Thickness 0.0280 in
DAM; UL94
HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
DAM; UL94
HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
DAM; IEC 60695-11-10
HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
DAM; IEC 60695-11-10
HB
@Thickness 0.710 mm
HB
@Thickness 0.0280 in
DAM; IEC 60695-11-10


电气性能

额定值 (公制)

额定值 (英制)

测试方法

相比耐漏电起痕指数(CTI) >= 600 V
@Temperature 23.0 °C
>= 600 V
@Temperature 73.4 °F
DAM; UL 746A


加工性能

额定值 (公制)

额定值 (英制)

测试方法

加工（熔体）温度 285 - 305 °C 545 - 581 °F DAM
295 °C 563 °F DAM; Optimum
模具温度 70.0 - 120 °C 158 - 248 °F DAM
100 °C 212 °F DAM; optimum
干燥温度 80.0 °C 176 °F DAM
干燥时间 2.00 - 4.00 hour 2.00 - 4.00 hour DAM
水分含量 <= 0.20 % <= 0.20 % DAM


材料描述



外观 Black Color DAM
Drying Recommended Yes, if moisture content of resin exceeds recommended level DAM
Filler Mineral filler DAM
形式 Pellets DAM
Generic Nylon 66 DAM
Material Status Current DAM
部件标识代码 >PA66-MD40< ISO 11469; DAM
Polymer Family Polyamide DAM
Polymer Type PA66 DAM
加工方法 Injection Molding DAM
产品分类 Low Warp Resins DAM
Mineral Reinforced Resins DAM
Mineral Reinforced Resins DAM
树脂识别 PA66-MD40 ISO 1043; DAM
符合RoHS指令 Contact Manufacturer DAM
特性: 尼龙作为大用量的工程原料,广泛用于机械.汽车.电器.纺织器材.化工设备.航空等领域。
成为各行业中不可缺少的结构材料，其主要特点如下：
1 优良的力学性能。尼龙的机械强度高韧性好。
2 自润性，摩擦性好。尼龙具有很好的自润性摩擦系数小，作为传动部件其使用寿命长。
3 优良的耐热性。如尼龙46等高结晶性尼龙的热变形温度很高，可在150℃下长期使用。PA66经过玻璃纤维增强以后，其热变形温度达到250℃以上
4 的电绝缘性能。尼龙的体积电阻很高，耐击穿电压高，是优良的电气，电器绝缘器材。
5 优良速度耐气候性。
6 吸水性。尼龙吸水性大，饱和水可达到3%以上。在一定程度影响制件的尺寸稳定性。
应用： 尼龙主要用于汽车配件、电气装置、交通运输业、机械制造工业、电线电缆通讯业、薄膜及日用品。