批发德国朗盛30玻纤PBT/PCPocanC3230LT

Density (23°C)

1.47

g/cm³

Apparent (Bulk) Density

0.80

g/cm³

Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)

14

cm³/10min

Tensile Modulus (23°C)

7800

MPa

Tensile Stress (Break, 23°C)

100

MPa

Tensile Strain (Break, 23°C)

2.4

%

Flexural Modulus 4 (23°C)

7700

MPa

Flexural Stress 4 (23°C)

155

MPa

Flexural Strain at Flexural Strength 5 (23°C)

2.5

%

Nominal Value

Unit

Test Method

Charpy Notched Impact Strength

-30°C

<10

kJ/m²

23°C

<10

kJ/m²

Charpy Unnotched Impact Strength

-30°C

35

kJ/m²

23°C

35

kJ/m²

Heat Deflection Temperature

0.45 MPa, Unannealed

165

°C

1.8 MPa, Unannealed

120

°C

Vicat Softening Temperature

150

°C

Melting Temperature 6

225

°C