- 名称：PA66玻纤增强10,安科罗PA66
- 联系：金龙 15916816001
原包安科罗PA66 AKROMID A3GF10玻纤增强10%
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ISO 1172 |
| Moisture Absorption | 2.6 - 2.8 % @Temperature 70.0 °C | 2.6 - 2.8 % @Temperature 158 °F | 62% r.h., Humidity; ISO 62 |
| Water Absorption at Saturation | 7.5 - 8.0 % @Time 82800 sec | 7.5 - 8.0 % @Time 23.0 hour | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 [mm/min]; ISO 527-1/2 |
| Elongation at Break | 20 % | 20 % | 5 [mm/min]; ISO 527-1/2 |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1[mm/min]; ISO 527-1/2 |
| Charpy Impact Unnotched | 11.6 J/cm² @Temperature 23.0 °C | 55.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
导电尼龙66：具有良好的耐磨性、耐热性、耐油性及耐化学药品性，还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。有很多金属和涂装的优点:零件重量较轻，较易处理，运输成本较低。它们的装配简便，制造成本较低，并且较不会受到撞凹，割损和刮伤。为了标识或美观目的，一些材料可被预先染色，避免费时且昂贵的两次着色加工。